4 Titanium Utility knives

[BladeMan]

Some recent Utility blades i made, all a little different.
All made from heat treated ATI425 Titanium with Ti screws/barrels, except for one.

This was a request for a longer then my normal Utility blade with white handle and double edge. Handle is Elforyn Super Tusk.
OAL is 9.85" with a 5.5" long and .114" thick blade. Weight is 2.78 oz.

Next was also a request, Harpoon blade with more belly, satin finish and sleek orange handle with lanyard pin. This knife will have a orange Kydex made and mounted on a Life Jacket for kayaking
Handle is Orange Jute (Burlap) Micarta with white G10 Liner.
OAL is 8.66" with a 4.3" long and .118" thick blade. Weight is 2.57 oz.

 

[BladeMan]

And while at it, i thought why not make my first Chisel grind, double edged.
Handle is Black and Mustard Jute Micarta with red G10 spacer and red and black G10 Liner.
OAL is 8.66" with a 4.3" long and .118" thick blade. Weight is 3.49 oz.

And last one, a super ultralight take on the same knife. Skeletonized with Paracord wrap and single edge with spine ridge.
OAL is 8.66" with a 4.3" long and .118" thick blade. Weight is 1.83 oz.

 

[tinfoil hat timmy]

all of those are sweet.

I especially like the hidden lanyard pin

 

[Dawkind]

All tremendous works my friend….

 

[betzner]

Lovin' it all, especially the one in paracord! All are really cool, Raimund............

 

[Dusty One]

All are Very Nice !

 

[Bigfattyt]

All fantastic.

 

[David Mary]

Beautiful! And I guess one could call that first one an "Elon(gated super) Tusk". Okay sometimes I can't help myself...

 

[woodysone]

Great looking and never rust, makes for a perfect old guys blade.

 

[Lorien]

that's some impressive work!
how do you like that alloy?

 

[jfk1110]

Wicked cool..

 

[BladeMan]

Thanks everyone!

Lorien , it is bitchy to work with but it makes a great blade for what i look for in a knife. Can also get it really sharp too.

 

[Lorien]

I researched it a tiny bit and couldn't find out whether or not it'll harden, (does it work harden?) but nothing conclusive so I expect probably not. Seems like it was developed to be more ductile than 6al4v, which may contribute to it taking a keen edge(?)